| AlF_3/N_2/空气气氛中密封熔炼镁试验研究 | |
| 聂书红 ; 熊守美 ; NIE Shu-hong ; XIONG Shou-mei | |
| 2010-06-08 ; 2010-06-08 | |
| 关键词 | 镁合金 密封炉 AlF3 表面膜 magnesium alloy sealed furnace AlF3 surface film TF822 |
| 其他题名 | Experimental Study on Melting Magnesium Under AlF_3/N_2/Air Protective Atmosphere |
| 中文摘要 | 在预先装入固态AlF3的密封熔炼炉中,研究了熔炼温度和炉内空气量对金属镁保护效果的影响,并对表面膜形貌、成分和成分分布进行了研究。研究结果表明,试验温度(≤800℃)下,熔炼温度和气氛中空气含量不影响金属镁的保护效果,金属镁很好被保护,熔炼温度和气氛中空气含量对表面膜成分和成分分布也没有明显影响;表面膜由MgF2区和MgF2+Al混合区域构成;所有表面膜致密,胞团直径小于0.5μm。固态AlF3在熔炼温度下蒸汽压高,汽化产物与金属镁反应生成MgF2和金属铝。; The effects of holding temperature and air content in the atmosphere on the protection of magnesium were investigated in a sealed furnace enclosed solid AlF3 before the experiments. The morphology, ingredients, and ingredient distribution of the surface film were also studied. The results showed that the Mg specimens were well protected at all experimental temperatures(≤800 ℃), holding temperature and air content in the atmosphere have no influence on the protection of magnesium, they also have no obvious influence on the composition of the surface film and its distribution in the surface film; All the surface films are made up of MgF2 zone and MgF2 +Al mixed zone, their morphology was a compact cellular structure with a smaller diameter than 0.5 цm. AlF3 has a high vapor pressure at the melting temperature, and the AlF3 vapor reacts with Mg, and changed into MgF2 and Al.; 清华-东洋镁铝合金成形技术研究开发中心项目; 博士后基金项目(2004035319)。 |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/48035]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 聂书红,熊守美,NIE Shu-hong,等. AlF_3/N_2/空气气氛中密封熔炼镁试验研究[J],2010, 2010. |
| APA | 聂书红,熊守美,NIE Shu-hong,&XIONG Shou-mei.(2010).AlF_3/N_2/空气气氛中密封熔炼镁试验研究.. |
| MLA | 聂书红,et al."AlF_3/N_2/空气气氛中密封熔炼镁试验研究".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论