	放电等离子烧结制备超高强度块体Al_(90)Mn_9Ce_1合金
	赵占奎 ; 姚可夫 ; 金松哲 ; 李敬锋 ; ZHAO Zhankui ; YAO Kefu ; JIN Songzhe ; LI Jingfeng
	2010-06-08 ; 2010-06-08
关键词	Al90Mn9Ce1合金 放电等离子烧结 成型性 准晶 Al90Mn9Ce1 alloy, spark plasma sintering, formability, quasicrystal TF124.5
其他题名	BULK Al_(90)Mn_9Ce_1 ALLOY WITH ULTRA-HIGH STRENGTH PREPARED BY SPARK PLASMA SINTERING
中文摘要	采用放电等离子烧结(spark plasma sintering)法在低压和低温(50 MPa和400-500℃)条件下快速烧结制备 出了含准晶强化相的块体Al90Mn9Ce1合金,其致密度大于98％,抗压强度超过1000 MPa．与普通高强度铝合金相比,其强 度约提高1倍．结果表明,在放电等离子烧结过程中,采用大电流、短时、低温的烧结条件可使快冷雾化法制备的原始台金粉末中 的准晶强化相及其它细小强化相得以保存,而局域强放电等离子体可以分解或破碎铝合金粉末表面的氧化膜,使合金粉末颗粒间的 结合强度增加,制备出的块体铝合金具有高的致密度和超高强度．; Using spark plasma sintering technique, a bulk Al90Mn9Ce1 alloy, reinforced by quasicrystal particles, has been sintered under the pressure of 50 MPa at 400 ℃. The density and the compressive strength of the as-prepared bulk alloy are above 98% and 1000 MPa, respectively. It has been found that during the spark plasma sintering process, under the condition of large current, short sintering time and lower sintering temperature, the metastable icosahedron quasicrystal phase in primary powder particles is kept. And the strong discharge plasma among particles can decompose or break the oxide film on the primary powder's surface, resulting in the increment of their combination strength. So the as-prepared bulk alloy possesses high density and ultra-high strength.; 中国博士后基金项目2003033133 清华大学基础研究基金项目091201107资助
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/47716]
专题	清华大学
推荐引用方式 GB/T 7714	赵占奎,姚可夫,金松哲,等. 放电等离子烧结制备超高强度块体Al_(90)Mn_9Ce_1合金[J],2010, 2010.
APA	赵占奎.,姚可夫.,金松哲.,李敬锋.,ZHAO Zhankui.,...&LI Jingfeng.(2010).放电等离子烧结制备超高强度块体Al_(90)Mn_9Ce_1合金..
MLA	赵占奎,et al."放电等离子烧结制备超高强度块体Al_(90)Mn_9Ce_1合金".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。