TiO_2/SiO_2/-γFe_2O_3-SiO_2磁性光催化剂的制备与表征 | |
王松威 ; 徐盛明 ; 陈崧哲 ; 徐景明 ; WANG Songwei ; XU Shengming ; CHEN Songzhe ; XU Jingming | |
2010-06-04 ; 2010-06-04 | |
关键词 | 氧化铁 氧化钛 氧化硅 磁性光催化剂 热稳定性 包覆 maghemite,titania,silica,magnetic photocatalyst,heat resistance,coating O643.36 |
其他题名 | Preparation and Characterization of TiO_2/SiO_2/γ-Fe_2O_3-SiO_2 Magnetic Photocatalyst |
中文摘要 | A γ-Fe_2O_3-SiO_2 composite was prepared by sol-gel method followed by calcination at 700 ℃ for 30 min starting from tetraethoxysilane and iron nitrate.Upon further coating with SiO_2 and TiO_2,a TiO_2/SiO_2/(γ-Fe_2O_3)-SiO_2 magnetic photocatalyst was obtained.XRD results show that Fe in the composite converts to the(γ-Fe_2O_3) phase up to a processing temperature of 700 ℃,and further increase in temperature results in the formation of the(α-Fe_2O_3) phase.The TiO_2/SiO_2/(γ-Fe_2O_3)-SiO_2 samples obtained are monodisperse spherical particles with 200~250 nm diameter,well coated firstly by an amorphous SiO_2 layer and then by an anatase TiO_2 layer.The TiO_2/SiO_2/(γ-Fe_2O_3)-SiO_2 particles retain their magnetic property well and show high activity for the photocatalytic degradation of salicylhydroxamic acid.; 国家自然科学基金资助项目(50274045) |
语种 | 中文 ; 中文 |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/36204] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | 王松威,徐盛明,陈崧哲,等. TiO_2/SiO_2/-γFe_2O_3-SiO_2磁性光催化剂的制备与表征[J],2010, 2010. |
APA | 王松威.,徐盛明.,陈崧哲.,徐景明.,WANG Songwei.,...&XU Jingming.(2010).TiO_2/SiO_2/-γFe_2O_3-SiO_2磁性光催化剂的制备与表征.. |
MLA | 王松威,et al."TiO_2/SiO_2/-γFe_2O_3-SiO_2磁性光催化剂的制备与表征".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论