| 纳米Ni(OH)_2的控制结晶法制备 | |
| 何向明 ; 李建军 ; 成宏伟 ; 姜长印 ; 万春荣 ; HE Xiang-Ming ; LI Jian-Jun ; CHENG Hong-Wei ; JIANG Chang-Yin ; WAN Chun-Rong | |
| 2010-06-04 ; 2010-06-04 | |
| 关键词 | 纳米Ni(OH)2 团聚控制 控制结晶 分散性 nano-scale nickel hydroxide controlled crystallization dispersive TM910.4 |
| 其他题名 | Preparation of Nano-scale Ni(OH)_2 Based on Controlled Crystallization |
| 中文摘要 | 纳米Ni(OH)2可以有效地提升镍氢电池的性能.本文以NiSO4和NaOH为原料,聚乙二醇为分散剂,采用控制结晶法制备了纳米Ni(OH)2的胶体溶液,控制结晶的pH值和温度分别为11.0和45℃.然后用正丁醇进行共沸蒸馏处理.制备了分散性良好的纳米Ni(OH)2粉体,粉体颗粒粒径20nm左右,团聚体系数为1.07.并用TEM和XRD对粉体进行了表征.所制备的样品在1C倍率放电时电容量达到258mAh·g-1。.; The dispersive nano-scale Ni(OH)2 was synthesized by a improved controlled crystallization process and dehydrated by azeotropic distillation with n-butanol. The pH value and temperature of controlled crystallization were optimized to be 11.0 and 45℃, respectively. As-prepared nano-scale Ni(OH)2 was dispersive, of 20nm size, and characterized by both TEM and XRD analysis. It had discharge capacity in excess of 258mAh·g-1.; 国家自然科学基金(50134020) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/35693]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 何向明,李建军,成宏伟,等. 纳米Ni(OH)_2的控制结晶法制备[J],2010, 2010. |
| APA | 何向明.,李建军.,成宏伟.,姜长印.,万春荣.,...&WAN Chun-Rong.(2010).纳米Ni(OH)_2的控制结晶法制备.. |
| MLA | 何向明,et al."纳米Ni(OH)_2的控制结晶法制备".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论