| 工艺参数对TiO_2溶胶黏度及胶凝时间的影响 | |
| 周锋 ; 傅迎庆 ; 梁开明 ; ZHOU Feng ; FU Ying-qing ; LIANG Kai-ming | |
| 2010-05-12 ; 2010-05-12 | |
| 关键词 | 二氧化钛 溶胶-凝胶法 黏度 胶凝时间 TiO2 sol-gel viscosity gel time TQ134.11 |
| 其他题名 | Effects of process parameters on viscosity and gel time of TiO_2 |
| 中文摘要 | 为获得稳定的TiO2溶胶,以钛酸四丁酯为先驱体,系统研究TiO2胶体的溶胶-凝胶转变过程,考察不同工艺条件对TiO2溶胶的黏度及胶凝时间的影响,并对其胶凝机理作了初步探讨.实验结果表明,获得稳定的TiO2溶胶的最佳工艺条件为:采用乙酰丙酮改性钛酸四丁酯,乙酰丙酮与钛酸四丁酯的摩尔比为1,水与醇盐的摩尔比为1,乙醇与醇盐的摩尔比为4,pH控制在2左右.; With Ti(OBu)4 as alkoxide precursor,sol-gel transition of TiO2 sol was studied to obtain steady TiO2 sol.The influence of different reaction conditions on viscosity and gel time was investigated,and the mechanism of sol-gel process was also researched.Experimental results show that the acetylacetone can greatly improve the stability of the sols and prolonging the gel time.The optimum preparation conditions are as follows: the molar ratio of acetylacetone to Ti(OBu)4 is 1,Ti(OBu)4 to water is 1,and alcohol to Ti(OBu)4 is 4,and the pH value of the solution is about 2. |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/28910]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 周锋,傅迎庆,梁开明,等. 工艺参数对TiO_2溶胶黏度及胶凝时间的影响[J],2010, 2010. |
| APA | 周锋,傅迎庆,梁开明,ZHOU Feng,FU Ying-qing,&LIANG Kai-ming.(2010).工艺参数对TiO_2溶胶黏度及胶凝时间的影响.. |
| MLA | 周锋,et al."工艺参数对TiO_2溶胶黏度及胶凝时间的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论