Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors | |
Wang, XF ; Gao, Q ; Liang, J | |
2010-05-10 ; 2010-05-10 | |
关键词 | supercapacitor electrochemical capacitor pseudo-capacitance ruthenium oxide carbon nanotubes OXIDE SUPERCAPACITOR Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering |
中文摘要 | The ruthenium oxide has been formed by a sol-gel process. The active electrode materials was obtained by mixing aqueous solution of RuCl(3)(.)xH(2)O and NaHCO3. The crystalline structure and the electrochemical properties of the powder have been studied as a function of the annealing temperature. At lower annealing temperatures, the powder is in an amorphous phase with a lower active surface area and poor electrochemical capacitance. The fine hydrous ruthenium oxide powder with satisfactory electrochemical characteristic was obtained by annealing the powder at 210 degrees C. The active surface area of the material is improved and the capacitance is calculated to be 540 F(.)g(-1). The composite with the carbon nanotubes as support was prepared. The capacitance of composite with 20wt% CNTs is calculated to be 860 F(.)g(-1). It is also found that the addition of carbon nanotubes in ruthenium oxide could improve the power characteristics of supercapacitors. |
语种 | 中文 ; 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH ; SHAANXI ; C/O RARE METAL MATERIAL ENGINEERING PRESS, PO BOX 51, XIAN, SHAANXI 710016, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/24629] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Wang, XF,Gao, Q,Liang, J. Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors[J],2010, 2010. |
APA | Wang, XF,Gao, Q,&Liang, J.(2010).Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors.. |
MLA | Wang, XF,et al."Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论