Fracture toughness of austempered high silicon cast steel | |
Chen, X ; Li, YX ; Fu, HG | |
2010-05-10 ; 2010-05-10 ; OCT | |
关键词 | fracture toughness austempering treatment high silicon cast steel COMPOSITION PROPERTY APPROACH HIGH-CARBON BAINITE MICROSTRUCTURE Metallurgy & Metallurgical Engineering |
中文摘要 | The influence of austempering treatment on the microstructure, retained austenite and fracture toughness of high silicon cast steel has been studied. The experimental results show that the retained austenite increases with increasing the austempering temperature, and the carbon contents in the retained austenite also shows a similar behavior. The fracture toughness of the steel firstly increases with increasing the austempering temperature, reaching a peak value of 63 MPa center dot m(1/2) at about 360-385 degrees C and then decreases. The maximum fracture toughness can be obtained for this steel when the microstructure contains about 30%-35% retained austenite. |
语种 | 中文 ; 中文 |
出版者 | SCIENCE PRESS ; BEIJING ; 16 DONGHUANGCHENGGEN NORTH ST, BEIJING 100717, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/23858] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Chen, X,Li, YX,Fu, HG. Fracture toughness of austempered high silicon cast steel[J],2010, 2010, OCT. |
APA | Chen, X,Li, YX,&Fu, HG.(2010).Fracture toughness of austempered high silicon cast steel.. |
MLA | Chen, X,et al."Fracture toughness of austempered high silicon cast steel".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论