Novel cobalt base superalloy and its high-temperature flow behavior | |
Tang Chunfeng ; Pan Feng ; Qu Xuanhui ; Duan Baihua ; Wang Tianjian ; He Xinbo | |
2010-05-10 ; 2010-05-10 | |
关键词 | cobalt base superalloy microstructure heat treatment hot compression deformation ALLOY NI CR Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering |
中文摘要 | A novel cobalt base superalloy containing titanium and aluminum was investigated through metallography, tensile test, and high-temperature isothermal compression deformation. The results show that proper content of titanium and aluminum with can improve the strength and ductility of the cobalt base superalloy. The Co-3(Ti,Al) compound with L 12 structure precipitates when the novel superalloy is aged at 800 degrees C for 20 h. The E phase with hcp structure also precipitates when the superalloy is deformed by 28% and then aged at 650 degrees C for 4 h. The E phase can exist at 800 degrees C. ne superalloy has excellent high-temperature mechanical properties. Its maximum flow stress at 850 degrees C is in the range of 360-475 MPa when the strain rate is between 0.0021 and 2.1 s(-1). The flow stress of the superalloy during high-temperature deformation can be described by the Zener-Hollomon parameter with a hot deformation activation energy of 397 kJ.mol(-1). |
语种 | 英语 ; 英语 |
出版者 | NONFERROUS METALS SOC CHINA ; BEIJING ; NO 30 XUEYUAN RD, BEIJING 100083, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/21704] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Tang Chunfeng,Pan Feng,Qu Xuanhui,et al. Novel cobalt base superalloy and its high-temperature flow behavior[J],2010, 2010. |
APA | Tang Chunfeng,Pan Feng,Qu Xuanhui,Duan Baihua,Wang Tianjian,&He Xinbo.(2010).Novel cobalt base superalloy and its high-temperature flow behavior.. |
MLA | Tang Chunfeng,et al."Novel cobalt base superalloy and its high-temperature flow behavior".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论