Influence of implanted aluminum ions on the oxidation behavior of M5 alloy at 500 degrees C | |
Peng, D. Q. ; Bai, X. D. ; Pan, F. ; Sun, H. ; Chen, B. S. | |
2010-05-10 ; 2010-05-10 | |
关键词 | M5 alloy air oxidation aluminum-ion implantation X-ray photoemission spectroscopy (XPS) auger-electron spectroscopy (AES) HIGH-TEMPERATURE CORROSION ZIRCALOY-4 IRON RESISTANCE CHROMIUM Metallurgy & Metallurgical Engineering |
中文摘要 | The beneficial effect of aluminum-ion implantation on the oxidation behavior of M5 alloy at 500 degrees C has been studied. M5 alloy specimens were implanted with aluminum ions with fluences ranging from 1 x 10(16) to 1 x 10(18) ions/cm(2), using a MEVVA source at a voltage of 40 kV at maximum temperature of 380 degrees C. The weight-gain curves were measured after oxidation in air at 500 degrees C for 120 min, which showed that a significant improvement was achieved in the oxidation behavior of M5 alloy implanted with aluminum compared with that of the as-received M5 alloy. The valences of elements in the implanted surface of M5 alloy were analyzed by X-ray photoemission spectroscopy (XPS), and the depth distributions of the elements in the surface of the samples were obtained by Auger-electron spectroscopy (AES). Scanning-electron microscopy (SEM) was used to examine the micro-morphology of oxidized samples. The color of the oxidized samples was checked by a scanner. Glancing-angle X-ray diffraction (GAXRD) at 0.3 degrees incident angles was employed to examine the phase transformations of implanted samples before and after oxidization in air at 500 degrees C for 120 min. It was found that when the fluence is 1 x 10(18) ions/ cm(2) the implanted M5 alloy is slightly oxidized. The mechanism of the improvement during oxidation is discussed. |
语种 | 英语 ; 英语 |
出版者 | SPRINGER/PLENUM PUBLISHERS ; NEW YORK ; 233 SPRING ST, NEW YORK, NY 10013 USA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/20249] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Peng, D. Q.,Bai, X. D.,Pan, F.,et al. Influence of implanted aluminum ions on the oxidation behavior of M5 alloy at 500 degrees C[J],2010, 2010. |
APA | Peng, D. Q.,Bai, X. D.,Pan, F.,Sun, H.,&Chen, B. S..(2010).Influence of implanted aluminum ions on the oxidation behavior of M5 alloy at 500 degrees C.. |
MLA | Peng, D. Q.,et al."Influence of implanted aluminum ions on the oxidation behavior of M5 alloy at 500 degrees C".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论