Cube texture development in pure Ni during annealing in a high strength magnetic field | |
Li, X ; Liu, W ; Godfrey, A ; Liu, Q | |
2010-05-10 ; 2010-05-10 | |
会议名称 | ICOTOM 14: TEXTURES OF MATERIALS, PTS 1AND 2 ; 14th International Conference on Textures of Materials ; Leuven, BELGIUM ; Web of Science ; INSPEC |
关键词 | cube texture recrystallization EBSP/EBSD magnetic field annealing Ni BOUNDARIES BICRYSTALS Materials Science, Multidisciplinary |
中文摘要 | A 10 Tesla magnetic field was applied during annealing of cold-rolled high purity Ni at 300 degrees C for 2 hours, with samples aligned at various different angles to the magnetic field direction. The effect of the magnetic field annealing on the cube texture evolution and the microstructural development was investigated by use of electron backscatter pattern (EBSP) analysis in the scanning electron microscope. The results show that both the cube texture evolution and the grain size are affected by the application during annealing of a high strength magnetic field, and that the effect varies as a function of the angle between the sample normal and the magnetic field direction. The cube texture volume fraction resulting from 2 hours annealing increases with increasing angle between the field direction and the sample normal direction, though in nearly all cases lower cube volume fractions were obtained compared to annealing without a magnetic field. The average size for all grains and for just cube-oriented grains both decrease with decreasing cube texture fraction, suggesting that the presence of a magnetic field either leads to enhanced recrystallization nucleation, or to a retardation of grain growth after recrystallization. |
会议录出版者 | TRANS TECH PUBLICATIONS LTD ; ZURICH-UETIKON ; BRANDRAIN 6, CH-8707 ZURICH-UETIKON, SWITZERLAND |
语种 | 英语 ; 英语 |
内容类型 | 会议论文 |
源URL | [http://hdl.handle.net/123456789/18184] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Li, X,Liu, W,Godfrey, A,et al. Cube texture development in pure Ni during annealing in a high strength magnetic field[C]. 见:ICOTOM 14: TEXTURES OF MATERIALS, PTS 1AND 2, 14th International Conference on Textures of Materials, Leuven, BELGIUM, Web of Science, INSPEC. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论