Effect of nano-calcium carbonate/pimelic acid bicomponent nucleating agent on polypropylene microporous membranes prepared via thermally induced phase separation | |
Luo Benzhe ; Zhang Jun ; Wang Xiaolin ; Wen Jianzhi | |
2010-05-07 ; 2010-05-07 ; OCT | |
关键词 | nano-CaCO3 pimelic acid nucleating agent thermally induced phase separation polypropylene microporous membrane ISOTACTIC POLYPROPYLENE CRYSTALLIZATION BEHAVIOR Polymer Science |
中文摘要 | Polypropylene (PP) microporous membranes were prepared with the composite diluents of soybean oil and di-n-butyl-phthalate (DBP) via thermally induced phase separation (TIPS). The effects of nano-CaCO3 nucleating agent and nano-CaCO3/pimelic acid bicomponent nucleating agent on the crystalline morphology and melting behaviors of the PP/soybean oil/DBP system, and on the microstructure of PP membrane were investigated. The experimental results showed that with addition of 0% similar to 4% single nano-CaCO3 nucleating agent the peak temperature of melting curve of PP in PP/soybean oil/DBP system varied from 150.7 degrees C to 151.3 degrees C while the peak melting temperature of pure PP is 165 degrees C. The differential scanning calorimetry (DSC) showed that the addition of bicomponent nucleating agent nano-CaCO3 (1% similar to 4%) and pimelic acid (0.5 %) induced two peaks on the melting curve. Wide-angle X-ray diffraction (WAXD) measurements proved that PP formed beta-phase and alpha-phase with addition of bicomponent nucleating agent nano-CaCO3 (1% similar to 4%) and pimelic acid (0.5 %) while the addition of single nano-CaCO3 nucleating agent resulted in only PP crystals of alpha-phase,which was consistent with the results of DSC. The addition of single nano-CaCO3 nucleating agent in PP/soybean oil/DBP system had unremarkable effect,on the morphology of PP membrane. While nano-CaCO3/pimelic acid (1 % /0.5 %) bicomponent nucleating agent was used, the PP microporous membrane showed smaller and regular pores. When the nano-CaCO3/pimelic acid content was 2%/0.5% and 4%/0.5%, PP microporous membrane showed more tiny irregular spherulites, as well as larger pores, which were related to the formation of beta phase. |
语种 | 中文 ; 中文 |
出版者 | SCIENCE CHINA PRESS ; BEIJING ; 16 DONGHUANGCHENGGEN NORTH ST, BEIJING 100717, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/17364] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Luo Benzhe,Zhang Jun,Wang Xiaolin,et al. Effect of nano-calcium carbonate/pimelic acid bicomponent nucleating agent on polypropylene microporous membranes prepared via thermally induced phase separation[J],2010, 2010, OCT. |
APA | Luo Benzhe,Zhang Jun,Wang Xiaolin,&Wen Jianzhi.(2010).Effect of nano-calcium carbonate/pimelic acid bicomponent nucleating agent on polypropylene microporous membranes prepared via thermally induced phase separation.. |
MLA | Luo Benzhe,et al."Effect of nano-calcium carbonate/pimelic acid bicomponent nucleating agent on polypropylene microporous membranes prepared via thermally induced phase separation".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论