Direct metal part forming of 316L stainless steel powder by electron beam selective melting | |
Qi, H. B. ; Yan, Y. N. ; Lin, F. ; He, W. ; Zhang, R. J. | |
2010-05-07 ; 2010-05-07 | |
关键词 | electron beam selective melting rapid manufacturing direct metal part forming 316L stainless steel powder Engineering, Manufacturing Engineering, Mechanical |
中文摘要 | Electron beam selective melting (EBSM) is a new type of rapid manufacturing of direct metal fabrication technology, which combines electron beam machining with rapid prototyping. It makes use of some advantages of an electron beam, such as high energy density, high absorption rate, and vacuum environment. In this study, direct metal part forming of gas and water-atomized 316L stainless steel powder were researched in detail. The one-dimensional experiments showed that the gas-atomized 316L stainless steel powder could be formed in a solid line at slow scanning velocity and low beam current while the water-atomized powder had serious balling and break-up phenomena at most conditions. The powder mixture containing 40-60 wt % of the gas-atomized powder has the optimum forming ability. The forming technology of the mixture powder must be divided into three steps: placing step, heating step, and melting step. After research on the technology parameters, some two-dimensional facets and three-dimensional parts were produced by EBSM. The microstructure of the three-dimensional forming parts was fine; the interfaces between the layers were metallurgically bonded. |
语种 | 英语 ; 英语 |
出版者 | PROFESSIONAL ENGINEERING PUBLISHING LTD ; WESTMINISTER ; 1 BIRDCAGE WALK, WESTMINISTER SW1H 9JJ, ENGLAND |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/15924] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Qi, H. B.,Yan, Y. N.,Lin, F.,et al. Direct metal part forming of 316L stainless steel powder by electron beam selective melting[J],2010, 2010. |
APA | Qi, H. B.,Yan, Y. N.,Lin, F.,He, W.,&Zhang, R. J..(2010).Direct metal part forming of 316L stainless steel powder by electron beam selective melting.. |
MLA | Qi, H. B.,et al."Direct metal part forming of 316L stainless steel powder by electron beam selective melting".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论