Chemical solution growth of CeO/sub 2/ buffer and YBCO layers on IBAD-YSZ/Hastelloy templates | |
Wang, S.S. ; Han, Z. ; Schmidt, W. ; Neumuller, H.W. ; Du, P. ; Wang, L. ; Chen, S. | |
2010-05-06 ; 2010-05-06 | |
关键词 | Experimental/ barium compounds buffer layers cerium compounds critical current density (superconductivity) high-temperature superconductors liquid phase deposition superconducting thin films superconducting transition temperature yttrium compounds/ chemical solution growth YBCO layers IBAD-YSZ/Hastelloy template coated conductors buffer layers solution molarity metalorganic deposition critical current density onset transition temperature transition width CeO/sub 2/ YBa/sub 2/Cu/sub 3/O/sub 7- delta // A8115L Deposition from liquid phases (melts and solutions) A7475 Superconducting films A7470V Perovskite phase superconductors A7460J Critical currents in type-II superconductors A6855 Thin film growth, structure, and epitaxy B0520J Deposition from liquid phases B3220H High-temperature superconducting materials/ CeO2/bin Ce/bin O2/bin O/bin YBa2Cu3O/ss Ba2/ss Cu3/ss Ba/ss Cu/ss O/ss Y/ss |
中文摘要 | Low-cost and commercially viable processes to fabricate coated conductors are necessary for application in electric-power technologies. We demonstrate the chemical solution growth of CeO/sub 2/ buffer and YBCO layers on IBAD-YSZ/Hastelloy templates. Very good biaxially textured CeO/sub 2/ buffer layers can be formed by the chemical solution method using inorganic cerium nitrate precursors. Through control of the solution molarity, very uniform, smooth, and dense CeO /sub 2/ buffer layers can be obtained. Subsequently, the YBCO films were deposited by metallorganic deposition using the trifluoroacetic (TFA-MOD) method. High-critical-current-density (J/sub c/) YBCO films were obtained, with the transport current density of about 1.2 MA cm/sup -2/ (77 K, 0 T). The onset transition temperature is as high as 94.5 K, and the transition width is about 1.3 K. Hence, the mature IBAD technique, combined with the low-cost solution method, can provide a very promising robust process for fabrication of low-cost YBCO coated conductor on a large scale. |
语种 | 英语 ; 英语 |
出版者 | IOP Publishing ; UK |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/15362] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Wang, S.S.,Han, Z.,Schmidt, W.,et al. Chemical solution growth of CeO/sub 2/ buffer and YBCO layers on IBAD-YSZ/Hastelloy templates[J],2010, 2010. |
APA | Wang, S.S..,Han, Z..,Schmidt, W..,Neumuller, H.W..,Du, P..,...&Chen, S..(2010).Chemical solution growth of CeO/sub 2/ buffer and YBCO layers on IBAD-YSZ/Hastelloy templates.. |
MLA | Wang, S.S.,et al."Chemical solution growth of CeO/sub 2/ buffer and YBCO layers on IBAD-YSZ/Hastelloy templates".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论