Electrosynthesis of soluble polythiophene derivatives with high thermal stability | |
Zhang, Z ; Tang, H ; Liang, X ; Shi, GQ | |
2010-05-06 ; 2010-05-06 | |
关键词 | polythiophene derivatives boron trifluoride diethyl etherate electrochemical polymerization conjugated polymer thermal stability TRIFLUORIDE DIETHYL ETHERATE ELECTROCHEMICAL POLYMERIZATION POLYMERS FILMS Chemistry, Analytical Electrochemistry |
中文摘要 | Poly(3-[4-(4-pentyl-cyclohexyl)-phenyl]-thiophene) (PPeChPhT) and poly(3-[2-fluoro-4-(4-pentyl-cyclohexyl)-phenyl]-thiophene) (PFPeChPhT) films were electrosynthesized by direct oxidation of the corresponding monomers in the mixed electrolytes of boron trifluoride diethyl etherate and ethyl ether (4:1, by volume). As grown PPeChPhT and PFPeChPhT films are in doped states and have conductivities of 0.10 and 0.11 S cm(-1), respectively. These two polymers in dedoped states are soluble in usual organic solvents such as tetrahydrofuran and chloroform, etc. The molar masses of the polymers were measured to be about 3400 g with dispersity of 1.32 (PPeChPhT) and 9300 g and dispersity of 1.51 (PFPeChPhT). Fluorescent spectral results showed that the polymers were strong yellow-green light emitters. Thermal degradation analysis results indicated that these polymers had high thermal stability with decomposition temperatures of about 500 degrees C. (c) 2005 Elsevier B.V. All rights reserved. |
语种 | 英语 ; 英语 |
出版者 | ELSEVIER SCIENCE SA ; LAUSANNE ; PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/12664] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Zhang, Z,Tang, H,Liang, X,et al. Electrosynthesis of soluble polythiophene derivatives with high thermal stability[J],2010, 2010. |
APA | Zhang, Z,Tang, H,Liang, X,&Shi, GQ.(2010).Electrosynthesis of soluble polythiophene derivatives with high thermal stability.. |
MLA | Zhang, Z,et al."Electrosynthesis of soluble polythiophene derivatives with high thermal stability".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论