Influence of structural evolution on energy storage properties in Bi0.5Na0.5TiO3-SrTiO3-NaNbO3 lead-free ferroelectric ceramics | |
Li, Feng1,2; Zhai, Jiwei1; Shen, Bo1; Liu, Xing1; Yang, Ke1; Zhang, Yang1; Li, Peng1; Liu, Baihui1; Zeng, Huarong2 | |
刊名 | JOURNAL OF APPLIED PHYSICS |
2017-02-07 | |
卷号 | 121期号:5 |
英文摘要 | Lead-free (1-x)(0.8Bi(0.5)Na(0.5)TiO(3)-0.2SrTiO(3))-xNaNbO(3) (x = 0-0.1, abbreviated as BNT-ST-xNN) ceramics were fabricated by a conventional sintering route with pure perovskite phase via XRD analysis. Raman spectrum was exploited in order to give an insight into the variation of local structural evolution. All compositions exhibited an obvious evolution of dielectric relaxation behaviors. Dielectric and ferroelectric properties clarified that a crossover from nonergodic to ergodic relaxor properties was obtained with the addition of NN content. A relatively large energy storage density was obtained W-Rec similar to 0.74 J/cm(3) at 7 kV/mm for x = 0.05 at room temperature. Particularly, the energy storage properties exhibited temperature (25-160 degrees C) and frequency stability (0.1-20Hz) with WRec around 0.6 J/cm(3) at 6 kV/mm for x = 0.05 within the ergodic region. Pulsed discharging current waveforms were measured under different electric fields to detect the energy storage density and discharging speed behavior. An illustration of the charge-discharge process for the nonergodic and ergodic relaxor was depicted in order to disclose the difference of energy storage properties in BNT-ST-xNN system, and it is believed that this concept can be a guideline for fixing a position when designing a new energy-storage system for BNT-based relaxor ferroelectric ceramics. Published by AIP Publishing. |
WOS标题词 | Science & Technology ; Physical Sciences |
类目[WOS] | Physics, Applied |
研究领域[WOS] | Physics |
关键词[WOS] | DIFFERENT ELECTRIC-FIELDS ; ANTIFERROELECTRIC CERAMICS ; POLYMER NANOCOMPOSITES ; RELAXOR FERROELECTRICS ; DENSITY CAPACITORS ; THIN-FILMS ; TITANATE ; BEHAVIOR ; PERFORMANCE |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000394345700017 |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/23551] |
专题 | 上海硅酸盐研究所_无机功能材料与器件重点实验室_期刊论文 |
作者单位 | 1.Tongji Univ, Sch Mat Sci & Engn, Funct Mat Res Lab, 4800 Caoan Rd, Shanghai 201804, Peoples R China 2.Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Funct Mat & Devices, Shanghai 200050, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Feng,Zhai, Jiwei,Shen, Bo,et al. Influence of structural evolution on energy storage properties in Bi0.5Na0.5TiO3-SrTiO3-NaNbO3 lead-free ferroelectric ceramics[J]. JOURNAL OF APPLIED PHYSICS,2017,121(5). |
APA | Li, Feng.,Zhai, Jiwei.,Shen, Bo.,Liu, Xing.,Yang, Ke.,...&Zeng, Huarong.(2017).Influence of structural evolution on energy storage properties in Bi0.5Na0.5TiO3-SrTiO3-NaNbO3 lead-free ferroelectric ceramics.JOURNAL OF APPLIED PHYSICS,121(5). |
MLA | Li, Feng,et al."Influence of structural evolution on energy storage properties in Bi0.5Na0.5TiO3-SrTiO3-NaNbO3 lead-free ferroelectric ceramics".JOURNAL OF APPLIED PHYSICS 121.5(2017). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论