Microstructure and properties of ferrite/organic nanocomposite prepared with microemulsion method

	Microstructure and properties of ferrite/organic nanocomposite prepared with microemulsion method
	Xu Zheng; Shuhui Yu; Rong Sun; Wenhu Yang; Ruxu Du
刊名	MATERIALS SCIENCE
	2012
英文摘要	A magnetite composite composed of the organic compounds and Fe3O4 nanoparticles was prepared with microemulsion method. The Tween 80 and ammonia were used as surfactant and reducing agent, respectively, in synthesizing the Fe3O4 nanoparticles. The experimental results showed that the composite possessed good stability while the volume ratio of Tween 80 to butanol was 0.4 and the molar ratio of NH4OH to Fe3+ was 14.6. The saturation magnetization of the composite depends on the molar ratio of NH4OH to Fe3+. The mechanism of this stable Fe3O4 paste was realized by the Fe3O4 nanocomposite film using TEM. The microstructures of the film show that the magnetic nanoparticles in the composite are surrounded by Tween 80, which separates the magnetic nanoparticles and leads to good stability.
收录类别	EI
原文出处	http://www.scientific.net/MSF.722.31
语种	英语
内容类型	期刊论文
源URL	[http://ir.siat.ac.cn:8080/handle/172644/3752]
专题	深圳先进技术研究院_集成所
作者单位	MATERIALS SCIENCE
推荐引用方式 GB/T 7714	Xu Zheng,Shuhui Yu,Rong Sun,et al. Microstructure and properties of ferrite/organic nanocomposite prepared with microemulsion method[J]. MATERIALS SCIENCE,2012.
APA	Xu Zheng,Shuhui Yu,Rong Sun,Wenhu Yang,&Ruxu Du.(2012).Microstructure and properties of ferrite/organic nanocomposite prepared with microemulsion method.MATERIALS SCIENCE.
MLA	Xu Zheng,et al."Microstructure and properties of ferrite/organic nanocomposite prepared with microemulsion method".MATERIALS SCIENCE (2012).