Synthesis and Low-Temperature Detemplation of High-Silica MFI Zeolite Membranes | |
Zhao Shu-Heng1,2; Lang Lin1![]() ![]() ![]() | |
刊名 | acta physico-chimica sinica
![]() |
2016-02-01 | |
卷号 | 32期号:2页码:519-526 |
关键词 | High-silica MFI zeolite membrane Template removal Low-temperature hydrocracking Gas permeation Support |
英文摘要 | high-silica mfi zeolite membranes supported on porous a-alumina discs were prepared by a seeded secondary growth method, using tetrapropylammonium hydroxide (tpaoh) as organic template. first, nanocrystals were deposited on rough alpha-al2o3 discs by a spin-on process. then, based on controlling the h2o/si molar ratio of the synthetic solution, a restricting in-plane hoh-oriented growth method with an ultra-dilute precursor was designed to prepare non-defective zeolite membranes that were as thin as possible. finally, cross linked and dense mr zeolite membranes were prepared after the third synthesis step, giving a membrane layer thickness of about 8 mu m, including similar to 5 mu m dense layers and 3 pm intermediate layers. a novel, two-step method, coupling by low-temperature hydrocracking and oxidation, is proposed for efficient removal of the template from zeolite membranes. compared with traditional high-temperature calcination, template removal by the two-step method could eliminate the grain boundary defects formed in response to stresses induced by heat treatment. as a result, the membranes treated by the two-step detemplation method displayed a preferable co2/n-2 separation factor (about 5.2) and high co2 permeance (5.8 x 10(-7) mol.m(-2).s(-1.)pa(-1)) at 30 degrees c. |
WOS标题词 | science & technology ; physical sciences |
类目[WOS] | chemistry, physical |
研究领域[WOS] | chemistry |
关键词[WOS] | template-removal ; separation performance ; molecular-sieve ; films ; zsm-5 ; permeation ; hydrocracking ; progress ; growth |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000371101900016 |
内容类型 | 期刊论文 |
源URL | [http://ir.giec.ac.cn/handle/344007/11128] ![]() |
专题 | 中国科学院广州能源研究所 |
作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, CAS Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Zhao Shu-Heng,Lang Lin,Jiang Jun-Fei,et al. Synthesis and Low-Temperature Detemplation of High-Silica MFI Zeolite Membranes[J]. acta physico-chimica sinica,2016,32(2):519-526. |
APA | Zhao Shu-Heng,Lang Lin,Jiang Jun-Fei,Yin Xiu-Li,&Wu Chuang-Zhi.(2016).Synthesis and Low-Temperature Detemplation of High-Silica MFI Zeolite Membranes.acta physico-chimica sinica,32(2),519-526. |
MLA | Zhao Shu-Heng,et al."Synthesis and Low-Temperature Detemplation of High-Silica MFI Zeolite Membranes".acta physico-chimica sinica 32.2(2016):519-526. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论