Sol-gel preparation of mesoporous Al2O3-SiO2 glasses: structural evolution monitored by solid state NMR | |
Ren, Jinjun; Zhang, Long; Eckert, Hellmut | |
刊名 | j. sol-gel sci. technol. |
2014 | |
卷号 | 70期号:3页码:482 |
关键词 | Silica-alumina Aluminum lactate Solid state NMR Mesoporous glasses |
通讯作者 | eckert, h (reprint author), univ munster, inst phys chem, corrensstr 30, d-48149 munster, germany. |
英文摘要 | glasses along the composition line 0.5al(2)o(3)-xsio(2) (1 a parts per thousand currency sign x a parts per thousand currency sign 6) were prepared via a novel sol-gel route using tetraethylorthosilicate and aluminum lactate as precursors. the structural evolution from solution to gel to glass is monitored by standard al-27 and si-29 nuclear magnetic resonance (nmr) spectroscopies, revealing important insights about molecular level mechanisms occurring at the various stages of glass formation. under the experimental conditions reported, silica and alumina precursors undergo homoatomic condensation processes when the gel is heat treated at about 100 and 300 a degrees c, respectively, and only little heteroatomic co-condensation occurs in this temperature range. the latter is promoted only upon elimination of the residual lactate and water ligands upon annealing the gels above 300 a degrees c. following calcination at 650 a degrees c, mesoporous glasses are obtained, having average pore diameter of about 3 nm and a surface areas near 500 m(2)/g. si-o-al connectivities are detected by si-29 magic angle spinning (mas)-nmr. al-27 mas-nmr spectra reveal aluminum in four-, five- and six-coordination. the spectra differ significantly from those of other sol-gel derived al2o3-sio2 materials prepared from different precursor routes, suggesting that the lactate route results in a higher degree of compositional homogeneity. |
收录类别 | SCI |
语种 | 英语 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.siom.ac.cn/handle/181231/13783] |
专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
作者单位 | 1.[Ren, Jinjun 2.Eckert, Hellmut] Univ Munster, Inst Phys Chem, D-48149 Munster, Germany 3.[Zhang, Long] Chinese Acad Sci, Shanghai Inst Opt & Fine Mech, Shanghai 201800, Peoples R China 4.[Eckert, Hellmut] Univ Sao Paulo, Inst Fis Sao Carlos, BR-13590 Sao Car |
推荐引用方式 GB/T 7714 | Ren, Jinjun,Zhang, Long,Eckert, Hellmut. Sol-gel preparation of mesoporous Al2O3-SiO2 glasses: structural evolution monitored by solid state NMR[J]. j. sol-gel sci. technol.,2014,70(3):482. |
APA | Ren, Jinjun,Zhang, Long,&Eckert, Hellmut.(2014).Sol-gel preparation of mesoporous Al2O3-SiO2 glasses: structural evolution monitored by solid state NMR.j. sol-gel sci. technol.,70(3),482. |
MLA | Ren, Jinjun,et al."Sol-gel preparation of mesoporous Al2O3-SiO2 glasses: structural evolution monitored by solid state NMR".j. sol-gel sci. technol. 70.3(2014):482. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论