温度梯度法生长大尺寸钛宝石晶体研究 | |
徐民; 司继良; 张小翠; 齐红基; 陈建玉 | |
刊名 | 人工晶体学报
![]() |
2014 | |
卷号 | 43期号:1页码:7 |
关键词 | 钛宝石晶体 温度梯度法 吸收特性 均匀性 位错密度 |
其他题名 | Study on Growth of Large-sized Ti: Al_2O_3 Crystals by the Temperature Gradient Technique |
中文摘要 | 采用温度梯度法生长了不同掺杂浓度的钛宝石(Ti:Al_2O_3)激光晶体,经退火加工获得的最大晶体尺寸达到ф86 mm*37 mm。室温下利用紫外-可见-近红外分光光度计测试了晶体300~1000 nm波段的吸收,分析了该系列晶体的吸收特性。结合晶体径向527 nm的吸收测试分析了晶体径向掺杂均匀性,同时使用Zygo干涉仪测试了晶体的光学均匀性,结果表明所生长的大尺寸钛宝石晶体具有良好的掺杂及光学均匀性。通过化学腐蚀法,利用光学显微镜观察表征了晶体位错密度,为2. 9 * 10~3/cm~2。 |
英文摘要 | Titanium-doped sapphire (Ti: Al_2O_3) crystals with different doping contents were grown by the temperature gradient technique, and the crystal with dimension of ф86 mm*37 mm was obtained. The absorption features of these crystals were analyzed through the results of absorption spectra measured by a ultraviolet/visible/near infrared (UV/Vis/NIR) spectrophotometer at room temperature over the range of 300-1000 nm. The radial doping uniformity of large-sized Ti: Al_2O_3 crystal was evaluated according to the absorption fluctuation at 527 nm, and the optical homogeneity was also determined by a Zygo interferometer. The dislocation density of Ti: Al_2O_3 crystal was characterized to be 2. 9 * 103/cm~2 with an optical microscope after etching the polished c-cut sample. |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:5085896 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.siom.ac.cn/handle/181231/12941] ![]() |
专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
作者单位 | 1.徐民, 中国科学院上海光学精密机械研究所, 中国科学院强激光材料重点实验室, 上海 201800, 中国. 2.司继良, 中国科学院上海光学精密机械研究所, 中国科学院强激光材料重点实验室, 上海 201800, 中国. 3.张小翠, 中国科学院上海光学精密机械研究所, 中国科学院强激光材料重点实验室, 上海 201800, 中国. 4.齐红基, 中国科学院上海光学精密机械研究所, 中国科学院强激光材料重点实验室, 上海 201800, 中国. 5.陈建玉, 中国科学院上海光学精密机械研究所, 中国科学院强激光材 |
推荐引用方式 GB/T 7714 | 徐民,司继良,张小翠,等. 温度梯度法生长大尺寸钛宝石晶体研究[J]. 人工晶体学报,2014,43(1):7. |
APA | 徐民,司继良,张小翠,齐红基,&陈建玉.(2014).温度梯度法生长大尺寸钛宝石晶体研究.人工晶体学报,43(1),7. |
MLA | 徐民,et al."温度梯度法生长大尺寸钛宝石晶体研究".人工晶体学报 43.1(2014):7. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论