大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究 | |
唐景平; 胡丽丽; 陈树彬; 陈伟; 王标; 翁泽安; 徐永春; 陈尤阔; 邹兆松; 胡俊江 | |
刊名 | 中国激光
![]() |
2015 | |
卷号 | 42期号:2页码:206003 |
其他题名 | Properties of Large Size N31 Nd:Phosphate Laser Glass Prepared by Continuous Melting |
通讯作者 | Tang Jingping, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Hu Lili, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Chen Shubin, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Chen Wei, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Wang Biao, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Weng Zean, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Xu Yongchun, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Chen Youkuo, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Zou Zhaosong, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Hu junjiang, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Wen Lei, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. ; Li Shunguang, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai 201800, China. |
中文摘要 | 报道了磷酸盐激光钕玻璃的连续熔炼线,以及采用连续熔炼工艺获得的400 mm 口径N31钕玻璃的主要性能。连熔所制备的N31-35钕玻璃的掺杂离子浓度为3.47(0.02)*10~(20)cm~(-3);1053 nm处的折射率为1.53360.0005;400 nm处的吸收系数平均值为0.098 cm~(-1); 1053 nm处的激光波长损耗为0.13~0.15% cm~(-1); 3000 cm~(-1)处的吸收系数平均值为0.83 cm~(-1)。400 mm 口径连熔N31钕玻璃的透射波前畸变在633 nm处小于A/3波长。采用1053 nm、脉冲为3 ns激光作用下连熔钕玻璃的体破坏阈值大于40 J/cm~2。结果表明,在N31钕玻璃的连续熔炼工艺中,除铂金和除水都取得了很好的效果。 |
英文摘要 | The continuous melting technology is reported. The 400 mm aperture N31 Nd:phosphate laser glass prepared from continuous melting technology is fabricated. The main properties of N31-35 glass have been disclosed. Its Nd~(3+) ion concentration is 3.47 (0.02)x 10~(20) cm~(-3). The refractive index at 1053 nm is 1.5336 0.0005. The absorption coefficients at 400 nm and 3000 cm~(-1), the laser wavelength loss at 1053 nm are 0.098 cm~1 and 0.83 cm 0.13~0.15% cm~(-1), respectively. The PV value of transmitted wavefront is less than A/3 at 633 nm. Its bulk damage threshold with 1053 nm, 3 ns pulse laser is larger than 40 J/cm~2. The results indicate that the dehydration and platinum particle removing processes are very effective during the continuous melting. |
收录类别 | EI |
原文出处 | http://www.opticsjournal.net |
语种 | 中文 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.siom.ac.cn/handle/181231/13853] ![]() |
专题 | 上海光学精密机械研究所_高功率激光单元技术研发中心 |
作者单位 | 1.唐景平, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 2.胡丽丽, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 3.陈树彬, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 4.陈伟, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 5.王标, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 6.翁泽安, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 7.徐永春, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 8.陈尤阔, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 9.邹兆松, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. 10.胡俊江, 中国科学院上海光学精密机械研究所激光玻璃研发中心, 上海 201800, 中国. |
推荐引用方式 GB/T 7714 | 唐景平,胡丽丽,陈树彬,等. 大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究[J]. 中国激光,2015,42(2):206003. |
APA | 唐景平.,胡丽丽.,陈树彬.,陈伟.,王标.,...&李顺光.(2015).大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究.中国激光,42(2),206003. |
MLA | 唐景平,et al."大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究".中国激光 42.2(2015):206003. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论