Efficiency-Enhanced Planar Perovskite Solar Cells via an Isopropanol/Ethanol Mixed Solvent Process | |
Mao, Peng1,2; Zhou, Qing1,2; Jin, Zhiwen1,2; Li, Hui1; Wang, Jizheng1,2 | |
刊名 | ACS APPLIED MATERIALS & INTERFACES
![]() |
2016-09-14 | |
卷号 | 8期号:36页码:23837-23843 |
关键词 | perovskite solar cell mixed solvent morphology component |
英文摘要 | Solution processable perovskite solar cells traditionally employed isopropanol as the solvent of CH3NH3I in a two-step method. One of the largest issues of this technique is the uncontrollable morphology of the perovskite film. In this study, a homogeneous and dense PbI2 filth was prepared by introducing DMSO as an additive into DMF and then reacting the mixture with CH3NH3I dissolved in an isopropanol/ethanol solvent to fabricate high-quality perovskite films. Results revealed that ethanol played a crucial role on morphology and components of perovskite films. When the ratio of isopropanol to ethanol was optimized, a power conversion,efficiency of 15.76% was achieved, which was on average, similar to 50% higher than that of PSCs without DMSO and ethanol processing. |
收录类别 | SCI |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/35294] ![]() |
专题 | 化学研究所_有机固体实验室 |
作者单位 | 1.Chinese Acad Sci, Inst Chem, CAS Key Lab Organ Solids, Beijing Natl Lab Mol Sci, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, 19 A Yuquan Rd, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Mao, Peng,Zhou, Qing,Jin, Zhiwen,et al. Efficiency-Enhanced Planar Perovskite Solar Cells via an Isopropanol/Ethanol Mixed Solvent Process[J]. ACS APPLIED MATERIALS & INTERFACES,2016,8(36):23837-23843. |
APA | Mao, Peng,Zhou, Qing,Jin, Zhiwen,Li, Hui,&Wang, Jizheng.(2016).Efficiency-Enhanced Planar Perovskite Solar Cells via an Isopropanol/Ethanol Mixed Solvent Process.ACS APPLIED MATERIALS & INTERFACES,8(36),23837-23843. |
MLA | Mao, Peng,et al."Efficiency-Enhanced Planar Perovskite Solar Cells via an Isopropanol/Ethanol Mixed Solvent Process".ACS APPLIED MATERIALS & INTERFACES 8.36(2016):23837-23843. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论