The high-temperature corrosion of Hastelloy N alloy (UNS N10003) in molten fluoride salts analysed by STXM, XAS, XRD, SEM, EPMA, TEM/EDS | |
Ye, XX; Ai, H; Guo, Z; Huang, HF; Jiang, L; Wang, JQ; Li, ZJ; Zhou, XT | |
刊名 | CORROSION SCIENCE
![]() |
2016 | |
卷号 | 106期号:-页码:249—259 |
关键词 | RAY ABSORPTION-SPECTROSCOPY NAF-KF SALT AISI 304-STAINLESS-STEEL REACTOR MSR ENVIRONMENTS SUPERALLOY FLINAK BEHAVIORS MOISTURE SYSTEMS |
ISSN号 | 0010-938X |
通讯作者 | Wang, JQ ; Li, ZJ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, 2019 Jia Luo Rd, Shanghai 201800, Peoples R China. |
英文摘要 | The effect of Fe ion impurity on the corrosion behavior of Hastelloy N (UNS N10003) alloy in molten FLi-NaK salts at 850 degrees C has been investigated by combined synchrotron radiation and other characterization techniques. Results showed that Mo and Cr were depleted from the alloy surface, where Fe-rich layer formed. The corrosion process was mainly controlled by the redox reaction between Fe ion and Cr, and no new compound with high valence state formed in the alloy surface. The loss of Mo and Cr in M12C carbide occurred due to the presence of a concentration-gradient between M12C carbide and matrix. (C) 2016 Elsevier Ltd. All rights reserved. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000373748600023 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/25867] ![]() |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Ye, XX,Ai, H,Guo, Z,et al. The high-temperature corrosion of Hastelloy N alloy (UNS N10003) in molten fluoride salts analysed by STXM, XAS, XRD, SEM, EPMA, TEM/EDS[J]. CORROSION SCIENCE,2016,106(-):249—259. |
APA | Ye, XX.,Ai, H.,Guo, Z.,Huang, HF.,Jiang, L.,...&Zhou, XT.(2016).The high-temperature corrosion of Hastelloy N alloy (UNS N10003) in molten fluoride salts analysed by STXM, XAS, XRD, SEM, EPMA, TEM/EDS.CORROSION SCIENCE,106(-),249—259. |
MLA | Ye, XX,et al."The high-temperature corrosion of Hastelloy N alloy (UNS N10003) in molten fluoride salts analysed by STXM, XAS, XRD, SEM, EPMA, TEM/EDS".CORROSION SCIENCE 106.-(2016):249—259. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论