The Effect of Grain Size and Dislocation Density on the Tensile Properties of Ni-SiCNP Composites During Annealing

CORC > 上海应用物理研究所 > 中国科学院上海应用物理研究所 > 中科院上海应用物理研究所2011-2017年

	The Effect of Grain Size and Dislocation Density on the Tensile Properties of Ni-SiCNP Composites During Annealing
	Yang, C; Huang, HF; Thorogood, GJ; Jiang, L; Ye, XX; Li, ZJ; Zhou, XT
刊名	JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
	2016
卷号	25 期号:3 页码:726—733
关键词	FLINAK SALT ENVIRONMENTS HALL-PETCH RELATION NANOCRYSTALLINE MATERIALS MICROCRACK FORMATION MILLING TIME MICROSTRUCTURE CORROSION BEHAVIOR ALLOYS RECRYSTALLIZATION
ISSN号	1059-9495
通讯作者	Huang, HF ; Zhou, XT (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, 2019 Jialuo Rd, Shanghai 201800, Peoples R China.
英文摘要	The grain size refinement, enhancement of mechanical properties, and static recrystallization behavior of metallic nickel-silicon carbide nano-particle (Ni-3wt.%SiCNP) composites, milled for times ranging from 8 to 48 h have been examined. One set of Ni-SiCNP composite samples were annealed at 300 A degrees C for 250 h, while the other set of samples were maintained at room temperature for control purposes (reference). The electron backscatter diffraction results indicate that the grain size of the annealed Ni-SiCNP composite was refined due to grain restructuring during static recrystallization. The x-ray diffraction results indicate that low-temperature annealing effectively reduced the density of dislocations; this can be explained by the dislocation pile-up model. Additionally, the tensile tests indicated that the annealed Ni-SiCNP composite had a significant increase in strength due to an increase of the Hall-Petch strengthening effect with a slight increase in the total elongation. The decrease of dislocation pile-up in the grain interiors and the increase in grain boundary sliding are assumed to be the main mechanisms at play. The relationship between the microstructural evolution and the variation of tensile properties is examined in this study.
收录类别	SCI
语种	英语
WOS记录号	WOS:000372309100002
内容类型	期刊论文
源URL	[http://ir.sinap.ac.cn/handle/331007/25863]
专题	上海应用物理研究所_中科院上海应用物理研究所2011-2017年
推荐引用方式 GB/T 7714	Yang, C,Huang, HF,Thorogood, GJ,et al. The Effect of Grain Size and Dislocation Density on the Tensile Properties of Ni-SiCNP Composites During Annealing[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2016,25(3):726—733.
APA	Yang, C.,Huang, HF.,Thorogood, GJ.,Jiang, L.,Ye, XX.,...&Zhou, XT.(2016).The Effect of Grain Size and Dislocation Density on the Tensile Properties of Ni-SiCNP Composites During Annealing.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,25(3),726—733.
MLA	Yang, C,et al."The Effect of Grain Size and Dislocation Density on the Tensile Properties of Ni-SiCNP Composites During Annealing".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE 25.3(2016):726—733.