HKT800 炭纤维缠绕成型复合材料性能 | |
顾红星![]() ![]() | |
刊名 | 固体火箭技术
![]() |
2016 | |
卷号 | 39期号:3页码:392-396 |
关键词 | 炭纤维 缠绕工艺 复合材料 性能 |
ISSN号 | 1006-2793 |
产权排序 | 1 |
中文摘要 |
为验证国产HKT800 炭纤维缠绕成型复合材料性能,分别用KH 树脂与WH、XA 和LN 树脂对比,在相同缠绕工艺下,制备了400 mm、150 mm 复合材料壳体和1. 6 L 复合材料压力容器,并进行了水压爆破试验。HKT800 炭纤维/KH树脂缠绕400 mm 壳体爆破压力达到了16. 2 MPa,150 mm 壳体爆破压力达到了34. 8 MPa,1. 6 L 容器爆破压力为89. 6 MPa。HKT800 炭纤维力学性能转化率可达到80 % 以上,充分证明湿法制备的T800 级炭纤维完全适用于缠绕成型工艺,基体树脂和成型工艺参数对缠绕成型复合材料器件性能均有较大影响。 |
英文摘要 |
In order to verify the properties of HKT800 carbon fiber composite in winding process,400 mm,150 mm composite shell and 1. 6 L pressure vessel were prepared with KH resin and other resin using the same winding process,and then the
water pressure blasting tests were carried out. Blasting pressure of 400 mm HKT800 carbon fiber /KH resin composite shell reaches 16. 2 MPa,and 150 mm shell reaches 34. 8 MPa,the explosion pressure of 1. 6 L composite pressure vessel is 89. 6 MPa,the mechanical properties conversion rate of HKT800 carbon fiber is more than 80 %,which prove T800 carbon fiber made by wet process is very suitable for winding process. The same reinforced carbon fibre,resin and winding process parameters has great impact
on the properties of its composites. |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:5766356 |
内容类型 | 期刊论文 |
源URL | [http://ir.opt.ac.cn/handle/181661/28155] ![]() |
专题 | 西安光学精密机械研究所_等离子体物理化学应用技术研究中心 |
作者单位 | 中国科学院西安光学精密机械研究所 |
推荐引用方式 GB/T 7714 | 顾红星,王浩静,薛林兵,等. HKT800 炭纤维缠绕成型复合材料性能[J]. 固体火箭技术,2016,39(3):392-396. |
APA | 顾红星,王浩静,薛林兵,赵佑军,&庞培东.(2016).HKT800 炭纤维缠绕成型复合材料性能.固体火箭技术,39(3),392-396. |
MLA | 顾红星,et al."HKT800 炭纤维缠绕成型复合材料性能".固体火箭技术 39.3(2016):392-396. |