Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide | |
Ma YW(马衍伟) | |
刊名 | JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
![]() |
2010 | |
通讯作者 | 马衍伟 |
中文摘要 | The effects of high magnetic field (10T) on the products obtained by calcination of Co-Fe LDH precursors at different temperatures were investigated. The XRD results indicated that Fe-III substituted for Co-III in Co3O4 to yield (CoCoFeO4)-Co-II-Fe-III-O-III under the calcination of Co-Fe LDH precursors at 400 degrees C. The products obtained by magnetic field annealing at 400 degrees C had a porous plate-like morphology, whereas the products without magnetic field annealing were composed of nanoparticles. It was seen that Co Fe2O4 phase could be formed at low temperature (about 500 degrees C) under the magnetic field annealing. The grain size of products obtained by magnetic field annealing at 800 degrees C was larger than that of zeromagnetic field. It was found that the saturation magnetization was significantly enhanced after magnetic field annealing, especially at lower temperature (<= 600 degrees C). The possible reason for the effects on the microstructure and magnetic properties of products obtained by magnetic field annealingwasdiscussed. |
学科主题 | 材料合成与加工工艺 |
收录类别 | 1 |
公开日期 | 2010-09-29 |
附注 | The effects of high magnetic field (10T) on the products obtained by calcination of Co-Fe LDH precursors at different temperatures were investigated. The XRD results indicated that Fe-III substituted for Co-III in Co3O4 to yield (CoCoFeO4)-Co-II-Fe-III-O-III under the calcination of Co-Fe LDH precursors at 400 degrees C. The products obtained by magnetic field annealing at 400 degrees C had a porous plate-like morphology, whereas the products without magnetic field annealing were composed of nanoparticles. It was seen that Co Fe2O4 phase could be formed at low temperature (about 500 degrees C) under the magnetic field annealing. The grain size of products obtained by magnetic field annealing at 800 degrees C was larger than that of zeromagnetic field. It was found that the saturation magnetization was significantly enhanced after magnetic field annealing, especially at lower temperature (<= 600 degrees C). The possible reason for the effects on the microstructure and magnetic properties of products obtained by magnetic field annealingwasdiscussed. |
内容类型 | 期刊论文 |
源URL | [http://ir.iee.ac.cn/handle/311042/389] ![]() |
专题 | 电工研究所_超导材料及强磁场科学研究组_超导材料及强磁场科学研究组_期刊论文 |
推荐引用方式 GB/T 7714 | Ma YW. Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS,2010. |
APA | 马衍伟.(2010).Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide.JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. |
MLA | 马衍伟."Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide".JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS (2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论