Strongly enhanced current-carrying performance in MgB2 tape conductors by C-60 doping | |
Ma YW(马衍伟) | |
刊名 | JOURNAL OF APPLIED PHYSICS |
2008 | |
通讯作者 | 马衍伟 |
中文摘要 | By utilizing C-60 as a viable alternative dopant, we demonstrate a simple and industrially scalable route that yields a 10 similar to 15-fold improvement in the in-high-field current densities of MgB2 tape conductors. For example, a J(c) value higher than 4x10(4) A/cm(2) (4.2 K, 10 T), which exceeds that for NbTi superconductor, can be realized on the C-60 doped MgB2 tapes. It is worth noting that this value is even higher than that fabricated using strict high energy ball milling technique under Ar atmosphere. At 20 K, H-irr was similar to 10 T for C-60 doped MgB2 tapes. A large amount of nanometer-sized precipitates and grain boundaries were found in MgB2 matrix. The special physical and chemical characteristics of C-60, in addition to its C containing intrinsic essence, are a key point in enhancing the superconducting performance of MgB2 tapes. |
学科主题 | 材料合成与加工工艺 |
收录类别 | 1 |
公开日期 | 2010-09-29 |
附注 | By utilizing C-60 as a viable alternative dopant, we demonstrate a simple and industrially scalable route that yields a 10 similar to 15-fold improvement in the in-high-field current densities of MgB2 tape conductors. For example, a J(c) value higher than 4x10(4) A/cm(2) (4.2 K, 10 T), which exceeds that for NbTi superconductor, can be realized on the C-60 doped MgB2 tapes. It is worth noting that this value is even higher than that fabricated using strict high energy ball milling technique under Ar atmosphere. At 20 K, H-irr was similar to 10 T for C-60 doped MgB2 tapes. A large amount of nanometer-sized precipitates and grain boundaries were found in MgB2 matrix. The special physical and chemical characteristics of C-60, in addition to its C containing intrinsic essence, are a key point in enhancing the superconducting performance of MgB2 tapes. |
内容类型 | 期刊论文 |
源URL | [http://ir.iee.ac.cn/handle/311042/321] |
专题 | 电工研究所_超导材料及强磁场科学研究组_超导材料及强磁场科学研究组_期刊论文 |
推荐引用方式 GB/T 7714 | Ma YW. Strongly enhanced current-carrying performance in MgB2 tape conductors by C-60 doping[J]. JOURNAL OF APPLIED PHYSICS,2008. |
APA | 马衍伟.(2008).Strongly enhanced current-carrying performance in MgB2 tape conductors by C-60 doping.JOURNAL OF APPLIED PHYSICS. |
MLA | 马衍伟."Strongly enhanced current-carrying performance in MgB2 tape conductors by C-60 doping".JOURNAL OF APPLIED PHYSICS (2008). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论