Controllable Low-Temperature Chemical Vapor Deposition Growth and Morphology Dependent Field Emission Property of SnO2 Nanocone Arrays with Different Morphologies | |
Li, XB ; Wang, XW(王学文) ; Shen, Q ; Zheng, J ; Liu, WH ; Zhao, H ; Yang, F ; Yang, HQ | |
刊名 | ACS APPLIED MATERIALS & INTERFACES |
2013-04-24 | |
卷号 | 5期号:8页码:3033-3041 |
关键词 | SnO2 nanocone arrays VS growth field-emission |
通讯作者 | Yang, HQ |
英文摘要 | Vertically aligned SnO2 nanocones with different morphologies have been directly grown on fluorine-doped tin oxide (FTO) glass substrates in a large area by heating a mixture of stannous chloride dihydrate (SnCl2·2H2O) and anhydrous zinc chloride (ZnCl2) at 600 °C in air. Control over the SnO2 nanocone arrays with different morphologies is achieved by adjusting the heat treatment time. The SnO2 nanocones are single crystalline with the tetragonal structure. A single-layer SnO2 nanoparticle film is first formed via the vapor–solid (VS) process due to the decentralization function of ZnCl2 vapor, and the SnO2 nanoparticles served as seeds and grew into nanocone arrays via the VS process. The sharp-tipped nanostructure formation may originate from a concentration gradient of reactant in the growth process. The as-obtained whiskerlike nanocone arrays exhibit enhanced field emission properties in comparison with typical nanoconelike structure arrays and other SnO2 nanostructured materials reported previously, and the turn-on field and field-enhancement factor is 1.19 V/μm and 3110, respectively. The experimental result is consistent with the Utsumi’s relative figure of merit for pillar-shaped emitters. |
收录类别 | SCI ; EI |
语种 | 英语 |
WOS记录号 | WOS:000318205000029 |
公开日期 | 2014-01-10 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinano.ac.cn/handle/332007/1274] |
专题 | 苏州纳米技术与纳米仿生研究所_纳米研究国际实验室_张珽团队 |
推荐引用方式 GB/T 7714 | Li, XB,Wang, XW,Shen, Q,et al. Controllable Low-Temperature Chemical Vapor Deposition Growth and Morphology Dependent Field Emission Property of SnO2 Nanocone Arrays with Different Morphologies[J]. ACS APPLIED MATERIALS & INTERFACES,2013,5(8):3033-3041. |
APA | Li, XB.,Wang, XW.,Shen, Q.,Zheng, J.,Liu, WH.,...&Yang, HQ.(2013).Controllable Low-Temperature Chemical Vapor Deposition Growth and Morphology Dependent Field Emission Property of SnO2 Nanocone Arrays with Different Morphologies.ACS APPLIED MATERIALS & INTERFACES,5(8),3033-3041. |
MLA | Li, XB,et al."Controllable Low-Temperature Chemical Vapor Deposition Growth and Morphology Dependent Field Emission Property of SnO2 Nanocone Arrays with Different Morphologies".ACS APPLIED MATERIALS & INTERFACES 5.8(2013):3033-3041. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论