Flat Panel X-ray Imaging of LuAG:Ce,Mg Ceramic Scintillators | |
Hu, C; Liu, SP; Feng ZD(冯召东)![]() ![]() | |
刊名 | JOURNAL OF INORGANIC MATERIALS
![]() |
2015 | |
卷号 | 30期号:8页码:814-818 |
关键词 | LuAG:Ce ceramic scintillators flat panel detector X-ray imaging Mg |
其他题名 | LuAG:Ce,Mg闪烁陶瓷的X射线平板探测器成像研究 |
英文摘要 | (Lu, Mg, Ce)(3)Al5O12 (LuAG: Ce, Mg) transparent ceramic scintillators (LuAG: 0.3at% Ce, 0.2at% Mg) with high optical and scintillation efficiency were fabricated by solid-state reaction method combined with vacuum sintering. The ceramic scintillator with dimension of 20 mm x 20 mm x 0.05 mm was packed with graphite substrate of 25 mm x 25 mm x 4 mm by graphite powders contained silica gel. Laser cutting of cubic array with dimension of 50 mu m x 50 mu m and distance of 10 mu m was performed. Flat panel X-ray imaging based on as prepaired ceramics was demonstrated. The images were good quality with a high resolution. The quality of the photos were evaluated by line-pair pattern method and knife edge method, respectively. MTF value of 17.5% was at 10 lp/mm for the ceramic scintillators after laser cutting, while resolution of 9 lp/mm achieved at 10% MTF by knife edge measurement. Based on above data, LuAG:Ce,Mg ceramics are proved to be a promising scintillator in flat panel X-ray imaging. |
学科主题 | Materials Science |
类目[WOS] | Materials Science, Ceramics |
收录类别 | SCI ; EI |
WOS记录号 | WOS:000361156200005 |
公开日期 | 2016-05-03 |
内容类型 | 期刊论文 |
源URL | [http://ir.ihep.ac.cn/handle/311005/228732] ![]() |
专题 | 中国科学院高能物理研究所 |
推荐引用方式 GB/T 7714 | Hu, C,Liu, SP,Feng ZD,et al. Flat Panel X-ray Imaging of LuAG:Ce,Mg Ceramic Scintillators[J]. JOURNAL OF INORGANIC MATERIALS,2015,30(8):814-818. |
APA | Hu, C.,Liu, SP.,冯召东.,秦秀波.,Feng, ZD.,...&Pan, YB.(2015).Flat Panel X-ray Imaging of LuAG:Ce,Mg Ceramic Scintillators.JOURNAL OF INORGANIC MATERIALS,30(8),814-818. |
MLA | Hu, C,et al."Flat Panel X-ray Imaging of LuAG:Ce,Mg Ceramic Scintillators".JOURNAL OF INORGANIC MATERIALS 30.8(2015):814-818. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论