基于主客体识别的光及温度双重敏感的形状记忆材料
方舸 ; 袁奇娟 ; 张晟 ; 李帮经
刊名高分子材料科学与工程
2014
卷号30期号:7页码:132-136
关键词主客体识别 形状记忆 双重响应型 α-环糊精
其他题名Light and Temperature Dual-Responsive Shape Memory Materials Based on Host-Guest Identification
通讯作者李帮经
产权排序1
合作状况其它
中文摘要首先分别制备了主体分子——海藻酸钠接枝的环糊精(Alg-α-CD)和客体分子——偶氮苯修饰的聚丙烯酸(PAAAzo)。然后通过化学交联得到Alg-α-CD/PAA-Azo化学交联膜。实验证明,由于α-CD-Azo可响应光波长变化和温度变化产生包合与解包合,Alg-α-CD/PAA-Azo化学交联膜表现出光和温度双重敏感型的形状记忆效应。其中,当光作为外界刺激时,材料的形状固定率达到85.8%±1.5%,形状回复率达到52.9%±1.9%;同样地,在温度刺激下,材料的形状固定率达到87.6%±4.2%,形状回复率达到43.37%±2.7%。
英文摘要Sodium algnate-grafted α-cyclodextrin ( Alg-α-CD) was prepared both as host molecule and azobenzenemodified polyacrylic acid ( PAA-Azo) was prepared as guest molecule firstly. Then Alg-α-CD/PAA-Azo film was obtained by chemical crosslinking. The results show that Alg-α-CD/PAA-Azo chemical cross-linking film exhibits light and temperature dual-sensitive shape memory effect since α-CD-Azo responds to wavelength changes and temperature change because of the photo-and temperature-sensitive inclusion between α-CD and Azo. When light is used as external stimuli, the fixity ratio achieves 85. 8% ± 1. 5% and the recovery ratio reaches 52. 9% ± 1. 9% . Similarly,using temperature as trigger,the fixity ratio achieves 87. 6% ± 4. 2% and the shape recovery rate reaches 43. 37% ± 2. 7%.
学科主题天然产物研究
收录类别CSCD
语种中文
CSCD记录号CSCD:5227481
内容类型期刊论文
源URL[http://210.75.237.14/handle/351003/26715]  
专题成都生物研究所_天然产物研究
推荐引用方式
GB/T 7714
方舸,袁奇娟,张晟,等. 基于主客体识别的光及温度双重敏感的形状记忆材料[J]. 高分子材料科学与工程,2014,30(7):132-136.
APA 方舸,袁奇娟,张晟,&李帮经.(2014).基于主客体识别的光及温度双重敏感的形状记忆材料.高分子材料科学与工程,30(7),132-136.
MLA 方舸,et al."基于主客体识别的光及温度双重敏感的形状记忆材料".高分子材料科学与工程 30.7(2014):132-136.
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace